Chemical treated BOPET film-nanocoating

Specifications Chemical treated BOPET film-nanocoating

1)Excellent tensile strength

2)High modules

3)Have high surface wetting tensions

Chemical treated BOPET film-nanocoating   Application: It it can be used for demanding places,at the same time it can replace part of foil composite packaging, use for higher water resistance, improve for liquid packaging. ,it can extend the shelf lift of contents, have an excellent fragrance retention, it can also used for pasteurization,also can be widely used for construction insulation materials such as lamination with non woven fabric.   Specification Thickness:12 micron etc Width :≤2100mm Paper core: 3”76mm  6” 152mm   Features: Using Dupon base materials,the surface have been chemical treated.and high adhesion between film and alumium layer after chemical treatment on the surface of film   Due to high adhesion of aluminium layer,No Al layer peels the shelf of life can be extended and have an excellent fragrance retention.  Higher reflection and heat preservation can be achieved by increasing the thickness of Al laye The water-proof nano resin on the aluminized surface have higher water resistance and higher heat preservation    Techinical data sheet:

Item		Unit	Test value	Test condition
Tensile strength	MD	Mpa	238	Temperature 23℃ Relative humidity 40%
	TD	Mpa	225
Elogoation at break	MD	%	126
	TD	%	126
Frication of Coefficient	The surface without Al plating/surface with Al plating	----	0.56
Equality of aluminized layer		%	±3
Fastness of the aluminized layer		%	No Aluminized layer peels
Wetting tension of Aluminum layer		Mn/m	58
Thickness of the aluminized layer		A	>890A
Reflective rate		%	95%	97%
Moisture vapor transmission rate		g/(m2·24h)	0.49	Temperature 38℃ Relative humidity :91%
Oxygen transmission rate		Cm3/(m2·24h·0.1Mpa)	0.75