Stainless Steel Welding Rods/Electrodes (AWS E308/E309/E310/E316/E317/E318/E347/E410/E430) - Find Your Match

Stainless Steel Welding Rods/Electrodes (AWS E308/E309/E310/E316/E317/E318/E347/E410/E430) - Find Your Match

$2.00 - $3.00/kilogram

Min. Order:: 1 kilogram

Min. Order:: 1 kilogram

Quantity:

Your message must be between 20 to 2000 characters

Contact Now

Basic Info

Supply Ability:	6000 Ton/Tons per Year
Payment Type:	L/C,T/T,Western Union

Product Description

We are factory!

("Shuanglu" and "SUNLU" for short), as a member of China Welding Association (CWA) and one of the appointed manufacturers of China National Electric Equipment Corporation (CNEEC), manufactures complete welding electrode product.

Packing:

2.5mm:2.5kg/box, 20kg/box, 2tons/pallet.

3.2mm:5kg/box, 20kg/box, 2 tons/pallet.

4.0mm:5kg/box, 20kg/box, 2 tons/pallet.

5.0mm:5kg/box, 20kg/box, 2 tons/pallet.

Or Customize!

Our factory supply:

AWS E6013,E7018,E6011, E6010,E308L-16 welding electrode and mig wire!

Market:

So far exported to Japan, Saudi Arabia, Qatar, USA,Brazil,Ukraine,Kenya,Thailand, India .etc.

Introduction:

E308L-16 is a kind of ultra-low-carbon Cr18Ni12Mo2 stainless steel electrode with lime-titania type coating. The carbon content of the deposited metal is lower than or equal to 0.04%. It has excellent heat-resistance, corrosion-resistance, crack-resistance, blowhole-resistance and welding performance. The coating has red-resistance and high strength. AC/DC.

Uses:

Used for welding equipment of urea, synthetic fiber, etc. and stainless steel structures of the same types, and also used for Cr stainless steel which does not need heat treatment after welding, composite steel, dissimilar steel, etc.

Chemical Composition of Deposited Metal (%)

Chemical Composition	C	Mn	Si	S	P	Ni	Mo	Cr
Guarantee Value	≤0.04	0.5~2.5	≤0.90	≤0.020	≤0.030	11.0~14.0	≤0.75	17.0~20.0

Mechanical Properties of Deposited Metal

Test Item	R_m(MPa)	A(%)	-196℃ KV2(J)
Guarantee Value	≥490	≥30	≥32

Reference Current (AC, DC+)

Electrode Diameter(mm)	φ2.0	φ2.5	φ3.2	φ4.0	φ5.0
Welding Current (A)	25~50	50~80	80~110	130~160	160~200

Instructions:
1.The electrodes should be baked under 250-300℃ for an hour before welding.
2.Direct current had better be used and the current should not be too strong.