Stainless steel cut wire shot(0.8mm)

Specifications Stainless steel cut wire shot(0.8mm)

Durability: 6000-6500 times

Certificate: ISO9001:2008, SAEJ441

Material:304,430,410

Stainless steel cut wire shot   Material: SUS304, SUS302, SUS430, SUS410 Size: 0.2mm - 2.5mm (else customized) Hardness: 308-509 HV (32-50HRC) Density: 7.8g/cm3 Durability: 6000-6500 times Certificate: ISO9001:2008, SAEJ441 Steel shot packing: 25kg/bag, 40bags/pallet,18-23 metric tons/container,or as customers request. Delivery: 7-10 days after the advance payment. Tianjin Xingang Port Payment Terms: T/T & L/C  

Main technical indicators of stainless steel shot
Product Description		Stainless steel round shot
Chemical composition(content)%	Carbon(C)	≤0.12%
	Manganese(Mn)	≤2.00%
	Silicon(Si)	≤1.00%
	Chromium(Cr)	17%~19%
	Nickel(Ni)	7%~9%
	Sulfur(S)	≤0.03%
	Phosphorus(P)	≤0.035%
Average hardness(measured under 500g load)		41~59HRC(338~509)HV
Hardness Deviation		±1.0HRC	±40HV

Application scope of stainless steel shot: Stainless steel shot cleaning: shot blasting cleaning, shot penning cleaning, cleaning of nonferrous aluminum alloy, copper alloy, magnesium alloy and zinc alloy die castings, shot blasting cleaning of stainless steel forgings, shot penning cleaning of forging, sand removing of casting, clean of stainless steel materials, cleaning of stainless steel sheets, surface burr removing of nonferrous pieces and smoothening, leveling, brightening and processing treatment. It can improve the anti-corrosion performance of work pieces, conceal the surface defects of castings and make product surface whitened and brightened. Stainless steel shot derusting: shot blasting derusting, derusting of forgings and steel plates, descaling of forgings and derusting of steels, H-shaped steels and steel structures. Stainless steel shot strengthening: shot blasting strengthening of stainless steel parts and shot penning strengthening of heat-treated pieces. Stainless steel shot penning: shot penning of nonferrous, copper, magnesium and zinc die castings and shot penning of stainless steel matericals.