High barrier coated polypropylene film
- Payment Type:
- L/C, T/T, Paypal, Western Union
- Incoterm:
- FOB, CFR, CIF
- Min. Order:
- 500 Kilogram
- Min. Order:
- 500 Kilogram
- Delivery Time:
- 25 Days
- Transportation:
- Ocean, Land, Air
- Port:
- Tianjin, Shanghai, Qingdao
Your message must be between 20 to 2000 characters
Contact Now| Place of Origin: | China |
|---|---|
| Productivity: | 5000mt |
| Supply Ability: | 5000 |
| Payment Type: | L/C,T/T,Paypal,Western Union |
| Incoterm: | FOB,CFR,CIF |
| Certificate: | CE,SGS,ROSH |
| Transportation: | Ocean,Land,Air |
| Port: | Tianjin,Shanghai,Qingdao |
High barrier coated polypropylene film
Pvdc Coated Film Description:
1.Stable adhering capacity and Special easy-peel & remove, no adhesive residue after the film removal;
2.We have the 9 whole production line (blow molding, printing, coating, cutting)
3.Pvdc Coated Bopp Film Use Glossy Bopp Filmas the backing material, one side coated high barrier PVDC can
do direct printing and composite on the coating.
Pvdc Coated Bopp Film feature:
1.Gas (O2, N2, CO2) barrier properties;
2.fragrance preserving performance;
3.Water vapor barrier property;
4.Oil and grease resistance;
5.Printing properties, transparency
Pvdc Coated Bopp Film Technical date sheet:
|
Test Item |
Test Method |
Unit |
Standard |
Test Results |
||
|
Width Tolerance |
GB/T 6673 |
mm |
+3.0 |
+3 |
||
|
Thickness Tolerance |
GB/T 6672 |
% |
±7.0 |
-5.4 |
||
|
Tension Strength |
MD |
GB/T 1040.3 |
MPa |
≥130 |
141.78 |
|
|
TD |
≥200 |
234.34 |
||||
|
Elongation Break |
MD |
GB/T 1040.3 |
% |
≤120 |
116.19 |
|
|
TD |
≤65 |
56.67 |
||||
|
Haze |
GB/T2410 |
% |
≤4.0 |
1.92 |
||
|
Friction coefficient |
Static |
GB/T 10006 |
/ |
≤0.80 |
0.50 |
|
|
Dynamic |
/ |
/ |
/ |
|||
|
Dyne(PVDC coated side corona treated) |
GB/T 14216 |
mN/m |
≥38 |
48 |
||
|
Moirture-vapor Transmission Rate |
GB/T 1037 |
g/(m2·24h) |
≤6.0 |
4.8 |
||
|
Oxygen Transmission Rate |
GB/T 19789 |
cm3/(m2·24h·0.1MPa) |
≤20.0 |
8.6 |
||
|
Non-Uniformity of End Faces |
/ |
mm |
≤2 |
0 |
||