ASTM A860 High-Strength Butt Welding Pipe Fittings
- Payment Type:
- L/C, T/T
- Incoterm:
- FOB, CFR, CIF
- Min. Order:
- 1 Piece/Pieces
- Min. Order:
- 1 Piece/Pieces
- Delivery Time:
- 15 Days
- Transportation:
- Ocean, Land, Air
- Port:
- Tianjin New Port, Shanghai Port, Beijing Air Port
Your message must be between 20 to 2000 characters
Contact Now| Place of Origin: | Cangzhou,China |
|---|---|
| Productivity: | 100pcs/week |
| Supply Ability: | 100pcs/week |
| Payment Type: | L/C,T/T |
| Incoterm: | FOB,CFR,CIF |
| Certificate: | CE/API/ISO |
| HS Code: | 73079300 |
| Transportation: | Ocean,Land,Air |
| Port: | Tianjin New Port,Shanghai Port,Beijing Air Port |
ASTM A860 is the standard specification for wrought high-strength ferritic steel Butt Weld Pipe Fitting of seamless and electric fusion-welded construction. These pipe fittings shall be furnished in accordance with the dimensions of Asme B16.9(for sizes NPS 14 and smaller) or Mss Sp-75 (for sizes NPS 16 through NPS 48). They can be further categorized into 6 grades: WPHY 42, WPHY 46, A860 Wphy52, A860 Wphy60, WPHY 65, A860 Wphy70. Pipe fittings manufactured to ASTM A860 are usually used with API 5L line pipes and ASTM A694 high-strength forged flanges in high-pressure gas and oil transmission and distribution systems.
A860wphy65 Elbow, 90° SCH120 L/R Elbow
1. Chemical Composition Requirements of ASTM A860
| The Chemical Composition of ASTM A860, % | |
|---|---|
| Carbon | ≤0.20*A |
| Manganese | 1.00-1.45 |
| Phosphorus | ≤0.030 |
| Sulfur | ≤0.010 |
| Silicon | 0.15-0.40*B |
| Nickel | ≤0.50*C |
| Chromium | ≤0.30*C |
| Molybdenum | ≤0.25*C |
| Copper | ≤0.35*C |
| Titanium | ≤0.05 |
| Vanadium | ≤0.10 |
| Columbium | ≤0.04 |
| Vanadium plus Columnium | ≤0.12 |
| Aluminum | ≤0.06 |
*The carbon equivalent C.E.=C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15 shall not exceed 0.42%.
*B If vacuum carbon deoxidation is used, silicon shall not exceed 0.10% by heat analysis and 0.12% by product analysis.
*C The sum of Ni+Cr+Mo+Cu shall not exceed 1.0%.
2. Mechanical Properties of ASTM A860
| ASTM A860/ 860M | Yield Strength, min. | Tensile Strength | Elongation, min. | Cv, avg./min. | |||
|---|---|---|---|---|---|---|---|
| Grade | ksi | MPa | ksi | MPa | % | ft*lbs | J |
| WPHY 42 | 42 | 290 | 60-85 | 415-585 | 25 | 30/25 | 40/34 |
| WPHY 46 | 46 | 315 | 63-88 | 435-605 | 25 | 30/25 | 40/34 |
| WPHY 52 | 52 | 360 | 66-91 | 455-625 | 25 | 30/25 | 40/34 |
| WPHY60 | 60 | 415 | 75-100 | 515-690 | 20 | 30/25 | 40/34 |
| WPHY 65 | 65 | 450 | 77-102 | 530-705 | 20 | 30/25 | 40/34 |
| WPHY 70 | 70 | 485 | 80-105 | 550-725 | 20 | 30/25 | 40/34 |
*1. The actual yield strength shall not exceed specified minimum by more than 15 ksi [105 MPa].
*2. The elongation values shall be measured on the basis of standard round specimen, or small-size proportional specimen, in 4D.
*3. The size of Charpy V-notch specimens shall be 10×10 mm while the impact-test temperature shall be −50°F[−46°C].
*4. All fittings of ASTM A860 shall have a maximum hardness of 22 HRC(235 HBW).
3. Material, Manufacture, Heat Treatment & Tests
The high-strength Pipe Fitting of ASTM A860 shall be made from fully killed fine-grain material made by a melting process that is intended to produce rounded, well dispersed, fine sulphide inclusions, that promote good notch toughness, assists in the resistance to hydrogen induced cracking, and for weldability suitable for field welding. The starting raw material may consist of plate, sheet, forgings, bar, seamless and fusion-welded pipes.
ASTM A860 WPHY 70, straight tees, 24inch SCH160.
All fittings shall be heat treatment by one of the methods of normalizing, quenching, tempering or stress relieving. The regular tests & inspections mainly include radiographic examination, ultrasonic test, Charpy V-Notch test, hardness test, etc. Especially, butt-weld tees manufactured by cold forming process shall be liquid penetrant or magnetic particle examined.