ASTM HDPE Column Point Geomembrane black
- Payment Type:
- L/C, T/T
- Incoterm:
- FOB, CFR, CIF
- Min. Order:
- 10000 Square Meter
- Min. Order:
- 10000 Square Meter
- Delivery Time:
- 15 Days
- Transportation:
- Ocean, Land
- Port:
- Tianjin Xingang Port
Your message must be between 20 to 2000 characters
Contact Now| Place of Origin: | Shandong china |
|---|---|
| Productivity: | 1000000 m2 |
| Supply Ability: | 1000000 m2 |
| Payment Type: | L/C,T/T |
| Incoterm: | FOB,CFR,CIF |
| HS Code: | 3920109090 |
| Transportation: | Ocean,Land |
| Port: | Tianjin Xingang Port |
HDPE column point geomembrane is a special designed geosythetic product widely used in human-made project as a waterproof and drainage material.It is usually used together with geotextile to provide seperation and water drainage function. Width, length and thickness of the membrane is various according to detail specification. It can also be welded by auto geomembrane welding machine.
Point evenly distributed with increased friction, and the appearance is very beautiful, The two sides of geomembrane can be hot melted together by different color and materials. We can set right side or reverse side of products according to geological conditions and project requirements. The product is produced by processing of hot-welt, extension in reasonable controlling, which increase products' tensile strength, puncture strength, abrasion resistance. It retains superior mechanical property and excellent elongation and stable chemical property of raw materials. And through adding functional agents in fixed proportion, which improved product's functions of anti-acid & alkali and anti-corrosion. It's tensile strength 3 times higher than normal I textured geomembrane.
Textured surface is specially designed to increase the sureface friction force so as to improve the stability of the building materials over it.
HDPE geomembrane with point Specifications(USA GRI-SM17 Standards)
|
Number |
Value |
Test value |
||||||
|
1.75mm |
1.0mm |
1.25mm |
1.5mm |
2.0mm |
2.5mm |
3.0mm |
||
|
1 |
Min Density/(g/cm2) |
0.939 |
||||||
|
2 |
Tensile properties |
|
|
|
|
|
|
|
|
|
Yield strength / (N/mm) |
11 |
15 |
18 |
22 |
29 |
37 |
44 |
|
Break strength / (N/mm) |
8 |
10 |
13 |
16 |
21 |
16 |
32 |
|
|
Yield elongation /% |
12 |
|||||||
|
Break elongation /% |
100 |
|||||||
|
3 |
Tear resistance /N |
93 |
125 |
156 |
187 |
249 |
311 |
374 |
|
4 |
Puncture resistance /N |
200 |
267 |
333 |
400 |
534 |
667 |
800 |
|
5 |
Stress crack resistance /h |
300 |
||||||
|
6 |
Carbon black |
|
|
|
|
|
|
|
|
|
Carbon black content /% |
2.0~3.0 |
||||||
|
|
Carbon black dispersion |
Carbon black dispersion(only near spherical agglomerates) for 10 different views 9 in categories 1or2and1 in category3 |
||||||
|
7 |
Oxidative induction time (OIT) |
|
|
|
|
|
|
|
|
|
Standard OIT-% retained after 90 days OIT/min |
100 |
||||||
|
|
High pressure OIT-% retained after 90 days OIT/min |
400 |
||||||
|
8 |
Oven aging at 85℃ |
|
|
|
|
|
|
|
|
|
Standard OIT -% retained after 90 days /% |
55 |
||||||
|
|
High pressure OIT -% retained after 90 days /% |
80 |
||||||
|
9 |
UV Resistance |
|
||||||
|
|
Standard OIT retained after 1600 hrs /% |
Not recommended since the high temperature of the Std-OIT test produces an unrealistic result for some of the antioxidants in the UV exposed samples |
||||||
|
|
High pressure OIT retained after 1600 hrs /% |
50 |
||||||
|
10 |
Low temperature impact brittle property at -70℃ |
pass |
||||||
|
11 |
Permeability g.cm/(cm2).Pa |
≤1.0X |
||||||
|
12 |
Dimensional stability /% Dimensional stability% |
±2 |
||||||
As to the detail specification, please contact us!